| ALLIAGE DE CUIVRE N° | CODE NO. DE LINGOT | NOMINAL COMPOSITION, GRADE, OR COMMERCIAL DESIGNATION | COMPOSITION, PER CENT MAXIMUM (UNLESS SHOWN AS A RANGE OR MINIMUM) | |||||||||||||
| Cu(1) | Sn | Pb | Zn(1) | Fe | Sb | Ni | S | P(2) | Al | Si | ||||||
| LAITONS ROUGES ET LAITONS ROUGES AU PLOMB | ||||||||||||||||
| 833 | 131 | 93-11/2-11/2-4 | 92.0-94.0 | 1.0-2.0 | 1.0-2.0 | 2.0-6.0 | -- | -- | -- | -- | -- | -- | -- | |||
| 834 | 407.5 | 90 cu:10 Zn | 88.0-92.0 | .20 | .50 | 8.0-12.0 | -- | -- | -- | -- | -- | -- | -- | |||
| 836(4) | 115 | 85-5-5-5 | 84.0-86.0(5) | 4.0-6.0 | 4.0-6.0 | 4.0-6.0 | .30 | .25 | 1.0(5) | .08 | .05 | .005 | .005 | |||
| 838(4) | 120 | 83-4-6-7 | 82.0-83.8(5) | 3.3-4.2 | 5.0-7.0 | 5.0-8.0 | .30 | .25 | 1.0(5) | .08 | .03 | .005 | .005 | |||
| LAITONS SEMI-ROUGES ET LAITONS SEMI-ROUGES PLOMBIFÈRES | ||||||||||||||||
| 842(4) | 101 | 80-5-2-13 | Cu(2) | Sn | Pb | Zn(2) | Fe | Sb | Ni | S | P(3) | Al | Si | |||
| 78.0-82.0 | 4.0-6.0 | 2.0-3.0 | 10.0-16.0 | -- | -- | -- | -- | -- | -- | -- | ||||||
| 844(4) | 123 | 81-3-7-9 | 78.0-82.0(5) | 2.3-3.5 | 6.0-8.0 | 7.0-10.00 | .40 | .25 | 1.0(5) | .08 | .02 | .005 | .005 | |||
| 845(4) | 125 | 78-3-7-12 | 77.0-79.0(5) | 2.0-4.0 | 6.0-7.5 | 10.0-14.0 | .40 | -- | 1.0(5) | -- | .02 | -- | -- | |||
| 848(4) | 130 | 76-3-6-15 | 75.0-77.0(5) | 2.0-3.0 | 5.5-7.0 | 13.0-17.0 | .40 | .25 | 1.0(5) | .08 | .02 | .005 | .005 | |||
| LAITONS JAUNES ET LAITONS JAUNES PLOMBIFÈRES | ||||||||||||||||
| 852 | 400 | 72-1-3-24 | Cu(2) | Sn | Pb | Zn(2) | Fe | Sb | Ni | S | P | AS | Al | Si | Mn | |
| 70.0-74.00 | .7-2.0 | 1.5-3.8 | 20.0-27.0 | .6 | .20 | 1.0 | .05 | .02 | -- | .005 | .05 | -- | ||||
| 853 | 407 | 70-30 Laiton Jaune | 68.0-72.0 | .50 | .50 | Rem. | -- | -- | -- | -- | -- | -- | -- | -- | (6) | |
| 854 | 403 | 67-1-3-29 | 65.0-70.0 | .50-1.5 | 1.5-3.8 | 24.0-32.0 | .7 | -- | 1.0 | -- | -- | -- | .35 | .05 | -- | |
| 855 | -- | 40-60 Laiton jaune | 59.0-63.0 | (7) | (7) | Rem. | (7) | -- | (7) | -- | -- | -- | -- | -- | (7) | |
| 856 | -- | 40-60 Laiton jaune | 59.0-63.0 | (7) | (7) | Rem. | (7) | -- | (7) | -- | -- | -- | -- | -- | (7) | |
| 857 | 405.2 | 63-1-1-35 | 58.0-64. | .50-1.5 | .8-1.5 | 32.0-40.0 | .7 | -- | 1.0 | -- | -- | -- | .55 | .05 | -- | |
| 858 | 405.1 | Moulage sous pression Y. B. | 57,0 min.(1,2) | 1.5 | 1.5 | 31.0-41.0 | .50 | .05 | .5 | .05 | .01 | .05 | .50 | .25 | .25 | |
| MANGANÈSE ET MANGANÈSE PLOMBIFÈRE | ||||||||||||||||
| 861 | 423 | 90 000 dizaines. Mn. Br. | Cu(2) | Sn | Pb | Zn(2) | Fe | Ni | Al | Mn | ||||||
| 66.0-68.0 | .20 | .20 | Rem. | 2.0-4.0 | -- | 4.5-5.5 | 2.5-5.0 | |||||||||
| 862 | 423 | 90 000 dizaines. Mn. Br. | 60.0-66.0 | .20 | .20 | 22.0-28.0 | 2.0-4.0 | 1.0 | 3.0-4.9 | 2.5-5.0 | ||||||
| 863 | 424 | 110 000 dizaines. Mn. Br. | 60.0-66.0 | .20 | .20 | 22.0-28.0 | 2.0-4.0 | 1.0 | 5.0-7.5 | 2.5-5.0 | ||||||
| 864 | 420 | 60 000 dizaines. Mn. Br. | 56.0-62.0 | .50-1.5 | .50-1.5 | 34.0-42.0 | .40-2.0 | 1.0 | .50-1.5 | .10-1.0 | ||||||
| 865 | 421 | 65 000 dizaines. Mn. Br. | 55.0-60.0 | 1.0 | .40 | 36.0-42.0 | .40-2.0 | 1.0 | .50-1.5 | .10-1.5 | ||||||
| 867 | 422 | 80 000 dizaines. Mn. Br. | 55.0-60.0 | 1.5 | .5-1.5 | 30.0-38.0 | 1.0-3.0 | 1.0 | 1.0-3.0 | 1.0-3.5 | ||||||
| 868 | -- | Nickel Mn. Bronze | 53.5-57.0 | 1.0 | .20 | Rem. | 1.0-2.5 | 2.5-4.0 | 2.0 | 2.5-4.0 | ||||||
| BRONZES AU SILICIUM ET LAITONS AU SILICIUM | ||||||||||||||||
| 872 | 500 | Silcion Br. (Everdur) | Cu | Sn | Pb | Zn | Fe | Al | Si | Mn | Mg | As | Sb | Ni | S | P |
| 89,0 min.(1) | 1.0 | .50 | 5.0 | 2.5 | 1.5 | 1.0-5.0 | 1.5 | -- | -- | -- | -- | -- | -- | |||
| 874 | 500 | Laiton au silicium | 79.0 Min, (1) | -- | 1.0 | 12.0-16.0 | -- | .8 | 2.5-4.0 | -- | -- | -- | -- | -- | -- | -- |
| 875 | 500 | 82-14-4 (tombasil) | 79.0 Min, (1) | -- | .50 | 12.0-16.0 | -- | .50 | 3.0-5.0 | -- | -- | -- | -- | -- | -- | -- |
| 876 | 500 | 89-6-5 | 88.0 Min, (1) | -- | .05 | 4.0-7.0 | -- | -- | 3.5-5.5 | -- | -- | -- | -- | -- | -- | -- |
| 878 | 500 | ZS 144 A | 80.0 Min, (1) | .25 | .15 | 12.0-16.0(2) | .15 | .15 | 3.8-4.2 | .15 | .01 | .05 | .05 | .20 | .05 | .01 |
| 879 | 500 | ZS 331 A | 63,0 min(1,2) | .25 | .25 | 30.0-36.0(2) | .40 | .15 | .8-1.2 | .15 | -- | .05 | .05 | .50 | .05 | .01 |
| BRONZES À L'ÉTAIN | ||||||||||||||||
| 902 | 242 | 92-8 | Cu(2) | Sn | Pb | Zn(2) | Fe | Sb | Ni | S | P | Al | Si | |||
| 91.0-94.0(9) | 6.0-8.0 | -- | .50 | -- | -- | -- | -- | -- | -- | -- | ||||||
| 903(4) | 225 | 88-8-0-4 | 86.0-89.0(5) | 7.5-9.0 | .30 | 3.0-5.0 | .20 | .20 | 1.0(5) | .05 | .05 | .005 | .005 | |||
| 905(4) | 210 | 88-10-0-2 | 86.0-89.0(5) | 9.0-11.0 | .30 | 1.0-3.0 | .20 | .20 | 1.0(5) | .05 | .05 | .005 | .005 | |||
| 907(4) | 205 | 89-11 Engrenage en Bronze | 88.0-90.0 | 10.0-12.0 | .50(10) | .50(10) | .15 | -- | (10) | -- | .10-.30 | .005 | -- | |||
| 908(4) | -- | 88-12 Engrenage en Bronze | 85.0-89.0(1) | 11.0-13.0 | .25 | .25 | .15 | .10 | .50 | .05 | .30 | .005 | .005 | |||
| 909 | 199 | 87-13 Bronze à l'étain | 86.0-89.0(1) | 12.0-14.0 | -- | -- | -- | -- | -- | -- | -- | -- | -- | |||
| 910(4) | 197 | 85-15 Bronze à l'étain | 84.0-86.0 | 13.0-15.0 | .20 | 1.5 | .10 | -- | .7(15) | -- | .05 | -- | -- | |||
| 911(4) | -- | 84-16 Bronze à l'étain | 82.0-85.0 | 15.0-17.0 | .25 | .25 | .25 | -- | -- | -- | 1.0 | -- | -- | |||
| 913(4) | 194 | 81-19 Bronze à cloche | 79.0-82.0 | 18.0-20.0 | .25 | .25 | .25 | -- | -- | -- | 1.0 | -- | -- | |||
| 916(4) | -- | 88-101/2-0-0-11/2 Ni | 86.0-89.0(1) | 9.7-10.8 | .25 | .25 | .15 | .10 | 1.2-2.0 | .05 | .25 | .005 | .005 | |||
| 917(4) | -- | 861/2-12-0-0-11/2 Ni | 84.0-87.0(1) | 11.3-12.5 | .25 | .25 | .15 | .10 | 1.2-2.0 | .05 | .30 | .005 | .005 | |||
| BRONZES AU PLOMB ET À L'ÉTAIN | ||||||||||||||||
| 922(4) | 245 | Marine 'M' | Cu(2) | Sn | Pb | Zn(2) | Fe | Sb | Ni | S | P | Al | Si | |||
| 86.0-90.0(5) | 5.5-6.5 | 1.0-2.0 | 3.0-5.0 | .25 | .20 | 1.0(5) | .05 | .05 | .005 | .005 | ||||||
| 923(4) | 230 | 87-8-1-4 | 85.0-89.0(5) | 7.5-9.0 | .30-1.0 | 2.5-5.0 | .25 | .20 | 1.0(5) | .05 | .05 | .005 | .005 | |||
| 924(4) | -- | -- | 86.0-89.0 | 9.0-11.0 | 1.0-2.5 | 1.0-3.0 | -- | -- | -- | -- | -- | -- | -- | |||
| 925(4) | 200 | 87-11-1-0-1 Ni | 85.0-88.0 | 10.0-12.0 | 1.0-1.5 | .50 | .30 | -- | .8-1.5 | -- | .20-.30 | .005 | -- | |||
| 926 | 215 | -- | 86.0-88.5 | 9.3-10.5 | .8-1.2 | 1.3-2.5 | .15 | -- | .7 | -- | .03 | -- | -- | |||
| 927(4) | 206 | 88-10-2 Pb | 86.0-89.0 | 9.0-11.0 | 1.0-2.5 | .7 | .15 | -- | 1.0 | -- | .25 | .005 | -- | |||
| 928(4) | 295 | 79-16-5 Pb | 78.0-82.0 | 15.0-17.0 | 4.0-6.0 | .50 | -- | -- | .50 | -- | -- | -- | -- | |||
| 929(4) | 206 W/N | 84-10-21/2-Pb-31/2 Ni | 82.0-86.0(1) | 9.0-11.0 | 2.0-3.2 | .25 | .15 | .10 | 2.8-4.0 | 0.05 | .50 | .005 | .005 | |||
| BRONZES À L'ÉTAIN À HAUTE TENEUR EN PLOMB | ||||||||||||||||
| 932(4) | 315 | 87-7-7-3 | Cu(2) | Sn | Pb | Zn(2) | Fe | Sb | Ni | S | P(3) | Al | Si | Total Autres | ||
| 81.0-85.0(5) | 6.3-7.5 | 6.0-8.0 | 2.0-4.0 | .20 | .35 | 1.0(5) | .08 | .15 | .005 | .005 | -- | |||||
| 934(4) | 310 | 84-8-8 | 82.0-85.0 | 7.0-9.0 | 7.0-9.0 | .7 | .15 | .50 | 1.0 | -- | .50 | -- | -- | -- | ||
| 935(4) | 326 | 85-5-9-1 | 83.0-86.0(5) | 4.3-6.0 | 8.0-10.0 | 2.0 | .20 | .30 | 1.0(5) | .08 | .05 | .005 | .005 | -- | ||
| 936 | -- | -- | 83,0 min. | 3.5-4.5 | 7.0-9.0 | 4.0 | .35 | .50 | 1.5 | -- | -- | -- | -- | .30 | ||
| 937(4) | 305 | 80-10-10 | 78.0-82.0(5) | 9.0-11.0 | 8.0-11.0 | .8 | .15(11) | .55 | 1.0(5) | .08 | .15 | .005 | .005 | -- | ||
| 938(4) | 319 | 78-7-15 | 75.0-79.0(5) | 6.3-7.5 | 13.0-16.0 | .8 | .15 | .8 | 1.0(5) | .08 | .05 | .005 | .005 | -- | ||
| 939(4) | -- | 77-6-16-1 | 76.5-79.5(5) | 5.0-7.0 | 14.0-18.0 | 1.5 | .40 | -- | .8(5) | -- | 1.5 | -- | -- | -- | ||
| 940(4) | 296 | 72-13-15 | 69.0-72.0(5) | 12.0-14.0 | 14.0-16.0 | .50 | .25 | .35 | .50-1.0(5) | -- | .05 | -- | -- | --(12) | ||
| 941(4) | 325 | 75-5-18-2 | 65.0-75.0(5) | 4.5-6.5 | 15.0-22.0 | 3.0 | -- | -- | -- | -- | -- | -- | -- | 1.0 | ||
| 942 | -- | -- | 68.5-75.5 | 3.0-4.0 | 21.0-25.0 | 3.0 | .35 | .50 | .50 | -- | -- | -- | -- | .40 | ||
| 943(4) | 322 | 71-5-24 | 68.5-73.5(5) | 4.5-6.0 | 22.0-25.0 | .8 | .15 | .8 | 1.0(5) | .08 | .05 | .005 | .005 | -- | ||
| 944(4) | 312 | 81-8-11 | Rem.(1) | 7.0-9.0 | 9.0-12.0 | .7 | .15 | .8 | 1.0 | -- | .20-.50 | -- | -- | -- | ||
| 945(4) | 321 | 73-7-20 | Rem. | 6.0-8.0 | 16.0-22.0 | 1.2 | -- | -- | -- | -- | -- | -- | -- | .7 | ||
| BRONZES AU NICKEL-ÉTAIN | ||||||||||||||||
| 947(4) | -- | 85-5-0-2-5 | Cu | Sn | Pb | Zn | Fe | Sb | Ni | S | P | Al | Mn | Si | ||
| 85.0-89.0 | 4.5-6.0 | .10(13) | 1.0-2.5 | .25 | .15 | 4.5-6.0 | .05 | .05 | .005 | .20 | .005 | |||||
| 948(4) | -- | 87-5-1-2-5 | 84.0-89.0 | 4.5-6.0 | .30-1.0 | 1.0-2.5 | .25 | .15 | 4.5-6.0 | .05 | .05 | .005 | .20 | .005 | ||
| 949(4) | -- | 80-5-5-5-5 | 79.0-81.0 | 4.0-6.0 | 4.0-6.0 | 4.0-6.0 | .30 | .25 | 4.0-6.0 | .08 | .05 | .005 | .10 | .005 | ||
| BRONZES D'ALUMINIUM | ||||||||||||||||
| 952 | 415 | 88-3-9 | Cu | Pb | Fe | Ni | Al | Mn | Si | |||||||
| 86.0 Min. (9) | -- | 2.5-4.0 | -- | 8.5-9.5 | -- | -- | ||||||||||
| 953 | 415 | 89-1-10 | 86.0 Min. (9) | -- | .8-1.5 | -- | 9.0-11.0 | -- | -- | |||||||
| 954 | 415 | 85-4-11 | 83.0 Min. (1) | -- | 3.0-5.0 | 2.5 | 10.0-11.5 | .50 | -- | |||||||
| 955 | 415 | Nickle Al. Bronze | 78.0 Min. (1) | -- | 3.0-5.0 | 3.0-5.5 | 10.0-11.5 | 3.5 | -- | |||||||
| 956 | -- | Silicium Al. Laiton | 88.0 Min. (9) | -- | -- | .25 | 6.0-8.0 | -- | 1.8-3.3 | |||||||
| 957 | -- | Mn-Ni-Al. Bronze | 71.0 Min. (9) | .03 | 2.0-4.0 | 1.5-3.0 | 7.0-8.5 | 11.0-14.0 | .10 | |||||||
| 958 | -- | 81-4-4-9-2 | 79.0 Min. (1) | .03 | 3.5-4.5 (16) | 4.0-5.0 (16) | 8.5-9.5 | .8-1.5 | .10 | |||||||
| CUIVRE-NICKELS | ||||||||||||||||
| 962(4) | -- | 90:10 Cuivre-Nickel | Cu | Pb | Fe | Ni | Mn | Si | Cb | C | Be | |||||
| 84.5-87.0 | .03(14) | 1.0-1.8 | 9.0-11.0 | 1.5 | .30 | 1.0 | .15 | -- | ||||||||
| 963 | -- | Rem.(2) | .03(14) | .40-1.0 | 18.0-22.0 | 1.0 | .7 | 1.0 | -- | -- | ||||||
| 964(4) | -- | 70:30 Cuivre-Nickel | 65.0-69.0 | .03(14) | .25-1.5 | 28.0-32.0 | 1.5 | .50 | .50-1.5 | .15 | -- | |||||
| 966 | -- | -- | Rem.(2) | .01 | .8-1.1 | 29.0-33.0 | 1.0 | .15 | -- | -- | .40-.7 | |||||
| NICKEL-ARGENT | ||||||||||||||||
| 973(4) | 410 | 57-2-9-20-12 | Cu | Sn | Pb | Zn | Fe | Sb | Ni | S | P | Al | Mn | Si | ||
| 530-58.0 | 1.5-3.0 | 8.0-11.0 | 17.0-25.0 | 1.5 | .35 | 11.0-14.0 | .08 | .05 | .005 | .50 | .15 | |||||
| 974 | 411 | 59-3-5-17-16 | 58.0-61.0 | 2.5-3.5 | 4.5-5.5 | Rem.(2) | 1.5 | -- | 15.5-17.0 | -- | -- | -- | .50 | -- | ||
| 976(4) | 412 | 64-4-4-8-20 | 63.0-67.0 | 3.5-4.5 | 3.0-5.0 | 3.0-9.0 | 1.5 | .25 | 19.0-21.5 | .08 | .05 | .005 | 1.0 | .15 | ||
| 978(4) | 413 | 66-5-2-2-25 | 64.0-67.0 | 4.0-5.5 | 1.0-2.5 | 1.0-4.0 | 1.5 | .20 | 24.0-27.0 | .08 | .05 | .005 | 1.0 | .15 | ||
| Notes: | ||||||||||||||||
| (1) | Le total des éléments nommés doit être d'au moins 99,5 %. | |||||||||||||||
| (2) | In reporting chemical analyses by the use of instruments such as spectrograph, X-ray, and atomic absorption, copper may be indicated as 'remainder'. In reporting chemical analyses obtained by wet methods, zinc may be indicated as 'remainder' on those alloys with over 2% zinc. | |||||||||||||||
| (3) | Pour les coulées continues, le phosphore maximum doit être de 1,5 %. | |||||||||||||||
| (4) | Ingot for remelting specifications vary from the ranges shown | |||||||||||||||
| (5) | Pour déterminer le cuivre minimum, le cuivre peut être calculé comme Cu + Ni | |||||||||||||||
| (6) | Autres éléments totaux, y compris l'étain et le plomb, 1,0 % maximum | |||||||||||||||
| (7) |
Sn + Pb + Ni + Mn + Fe: Total 1.0% maximum; .20% maximum for each element |
|||||||||||||||
| (8) | Le total des éléments nommés doit être d'au moins 99,8 %. | |||||||||||||||
| (9) | Le total des éléments nommés doit être d'au moins 99,0 %. | |||||||||||||||
| (10) | Les teneurs totales en Pb, Zn et Ni ne doivent pas dépasser 1,0 %. | |||||||||||||||
| (11) | L'acier doit contenir un maximum de 0,35 % de fer lorsqu'il est utilisé pour les paliers à dos en acier. | |||||||||||||||
| (12) | For continuous castings, sulfur shall be .25% maximum, and total other elements .35% maximum | |||||||||||||||
| (13) | The mechanical properties of copper alloy No. 947 (heat treated) may not be attained if the lead content exceeds .01% | |||||||||||||||
| (14) | Pour les nuances de soudage, la teneur en plomb ne doit pas dépasser 0,01 %. | |||||||||||||||
| (15) | Nickel is a residual element and shall not be intentionally added to the melt | |||||||||||||||
| (16) | La teneur en fer ne doit pas dépasser la teneur en nickel | |||||||||||||||
Nous nous concentrons sur la fourniture de concasseurs de haute qualité et de pièces d'usure pour concasseurs.
Concasseur à cône Symons 2 pieds, 3 pieds, 4,25 pieds, 5,5 pieds, 7 pieds.
Sandvik CH420, CH430, CH440, CH660, CH880, CS420, CS430, CS440, CS660.
HP100, HP200, HP300, HP400, HP500, HP700, HP800.
Et portez des pièces de rechange pour d'autres concasseurs courants.
CHANGSHA TIGER MACHINERY CO., LTD.
106-7#,No.163 building Tianhuabeilu,Changsha county, Hunan,China
Tél:
+86-187 7489 4905
WhatsApp :
+86-187 7489 4905
WeChat :
+86-187 7489 4905
Email:
©2025 CHANGSHA TIGER MACHINERY CO., LTD.